Method
|
|
|
General
|
Core Composition
|
SiO2 + GeO2
|
|
|
Clad Composition
|
SiO2
|
|
|
Refractive Index Profile
|
Step Index, Matched Cladding
|
|
|
Optical Properties
|
Attenuation
|
<= 0.344 dB/km (at 1310nm)
< = 0.204 dB/km (at 1550nm)
|
EIA/TIA-61, 78
|
|
Attenuation Uniformity
|
<=0.05dB at 1310 & 1550nm
|
EIA/TIA-61
|
|
Attenuation at Water Peak
|
<= 1.0dB/km at 1383 3nm
|
EIA/TIA-78
|
|
Attenuation (1285 – 1330nm)
|
<= Measured Attenuation at
1310nm +
0.05dB/km
|
EIA/TIA-78
|
|
Attenuation (1525 – 1575nm)
|
<=Measured Attenuation at
1550nm +
0.05dB/km
|
EIA/TIA-78
|
|
Fiber Cutoff Wavelength
|
1190 ~ 1330nm
|
EIA/TIA-80
|
|
Cabled Cutoff Wavelength
|
<=1260nm ±
|
EIA/TIA-170
|
|
MFD
|
9.3
0.5 µm
(at 1310nm)
10.5
1.0 µm (at
1550nm)
|
EIA/TIA-167
|
|
Bending Loss (100turns, 60mm)
|
< = 0.05dB (at 1310 nm)
< = 0.10 dB (at 1550 nm)
|
EIA/TIA-62
|
|
Bending Loss (1turn, 32mm)
|
<=0.50dB (at 1550)
|
EIA/TIA-62
|
|
Zero-dispersion Wavelength (λο)
|
±±1300
~ 1322 nm
|
EIA/TIA-175
|
|
Dispersion Slope at λο
|
<=0.092 ps/(nm2·km)
|
EIA/TIA-175
|
|
Dispersion in 1285-1330nm
|
<=3.5 ps/(nm·km)
|
EIA/TIA-175
|
|
Dispersion at 1550nm
|
<=18ps/(nm·km)
|
EIA/TIA-175
|
|
Polarization Mode Dispersion
|
<=0.2psec/sqrt km at 1310nm
|
EIA/TIA-122
|
|
Dimensional
&
Mechanical
Properties
|
Clad Dia.
|
125
1.0 µm
|
EIA/TIA-176
|
|
Clad Non-Circularity
|
< = 1.0 %
|
EIA/TIA-176
|
|
Coated Dia.
|
245
10 µm
|
EIA/TIA-173
|
|
Coating/Clad Concentricity Error
|
< = 12 µm
|
EIA/TIA-173
|
|
Coating Strip Force
|
1.3N<F<8.9N at ± 0oC
to +45oC
|
EIA/TIA-178
|
|
Fiber Curl (Radius)
|
>=4m
|
EIA/TIA-111
|
|
Core/Clad Concentricity Error
|
<=0.8± µm
|
EIA/TIA-176
|
|
Tensile Strength (Unaged, 1m)
|
50% Weibull Probability >= 3.8
GN/m2
|
EIA/TIA-28
|
|
Proof Test Stress
|
< =0.7 GN/m2
|
EIA/TIA-31
|
|
Environmental Specification
|
Temperature Cycling (-60 ~85oC)
|
Induced Attenuation <=
0.05dB/km At 1310 & 1550nm
|
EIA/TIA-3
|
|
Operating Temperature Range
|
-60 ~ 85oC
|
EIA/TIA-69
|
|
|
|
|